- Laser Beauty Equipment[3]
- Other Active Components[1]
- Other Optics Instruments[10]
- Glass Processing Machinery[3]
- Glass Product Making Machinery[1]
- Other Electronic Components[3]
- Other Passive Components[1]
- Other Lights & Lighting Products[6]
- Instrument Parts & Accessories[3]
- Loose Gemstone[1]
- Other Metals & Metal Products[1]
- Laser Equipment Parts[1]
- Halide ( Except Chloride )[2]
- Prisms[4]
- Lenses[2]
- Refractory[1]
- Chemical Reagents[1]
- Fiber Optic Equipment[5]
- Chemical Auxiliary Agent[3]
- Other Ore[1]
- Building Glass[1]
- Contact Person : Mr. Ge Alex
- Company Name : Atom Optics Co., Ltd.
- Tel : 00086-21-39523288
- Fax : 00086-21-39523268
- Address : Shanghai,shanghai,No.1661-14-101 Baojia Road Jiading District Shanghai 201808 of China
- Country/Region : China
- Zip : 201808
KTP Electro-optic Q-Switch
Regular flux grown KTP has an electric resistivity as low as 106 W×cm, which may exhibit the detrimental electrochromism when subjected to a dc electric field. Electro-optic KTP (EO-KTP) crystals with high electrical resistivity (~1011-1012W·cm) have been grown successfully using our own proprietary technology. The electrochromism is not observed under a continuous 500V/mm Z-directed electric field over more than 1000 hours. The well-known isomorphs RTP performance given applies also to EO-KTP which has high damage threshold, large effective electro-optic coefficients and lower half-wave voltage. The Q-switch is built utilizing thermally compensated double-crystal designsAdvantages:
High Damage Threshold No Piezoelectric RingingLow Insertion LossThermal Compensating DesignNon-hygroscopicHigh Extinction and Contrast RatioSpecifications
Spectral range: 350nm~4500nm
Half Wave Voltage at 1064 nm: 5x5x10 mm: ~1,600 V 8x8x10 mm: ~2,600 V 9x9x20 mm: ~1,450 V
Contrast ratio: >2001
Aperture: from 2x2 mm² up to 15x15 mm²
Damage threshold: > 750MW/cm2 (@ 1064nm, 10ns, 10Hz)
AR coating: R < 0.2% @ 1064 nm